Material Witness: Low-Flow Prepregs–Defining the Process


Reading time ( words)

One of my favorite authors once wrote about perception:  “For now we see in a mirror, dimly…” speaking in an era when mirrors were at best polished metal surfaces.  In the infancy of low-flow products, we used to speak about “no-flow” prepregs as if “no-flow” was sufficient definition of the product, but as we have recently pointed out in our discussions of rheology, “everything flows.” And as we consider these increasingly essential but sometimes hard-to-define products, much consideration will have to be given to what the products need to do, how they do it, how we test them, what the testing means, and how or if the testing relates meaningfully to how the products work in a PWB rigid-flex production environment.

Let’s try to define “low flow” in terms that will make sense to both suppliers and users of the products.  A low-flow prepreg is a prepreg that flows sufficiently to wet out and adhere to bonding surfaces and to fill inner layer copper details, but does not flow so much as to fill in cut-out areas in a heat sink or run unevenly out of the interface between rigid and flexible elements of a rigid-flex PWB.  That being said, how to define that flow quantitatively and to control it in such a way that the resulting product has wide applicability in a variety of PWB heat-sink and rigid-flex designs has been an issue with both producers and users of the products since the introduction of the concept.  (My personal involvement in low flow materials began in the Early Mesozoic Period.)

 

guiles new Fig1.JPG

Guiles Fig2.JPG

How low is low flow compared to “normal” prepregs?  Figure 1, the chart labeled as 35N Rheology, and Figure 2, 47N Rheology, are respectively a standard polyimide prepreg—35N—with a minimum viscosity about 800 poise at heat-up rate 5oC/minute, and a standard epoxy low-flow product—47N—with  a minimum viscosity about 8000 poise at heat-up rate of 5oC/minute. As you can see, the viscosity of the low-flow product is about an order of magnitude higher than that of the full-flow prepreg. 

Note also that as the heat-up rate is adjusted, the minimum viscosity of the low-flow product behaves similar to that of a standard-flow resin.  As the heat-up rate increases, the minimum melt viscosity is lower, and hence, the product will flow more, all other conditions being equal.  If only it were practical to use a three-temperature ramp rate test to characterize low-flow products during manufacture! 

Instead, we have an IPC test procedure (IPC TM-650 2.3.17.2) that defines low flow in terms of average reduction of the diameter of a cut-out circle when the material is tested under “standard” conditions of temperature and pressure. 

Share

Print


Suggested Items

Altium Introduces New Subscription Model

02/25/2021 | Andy Shaughnessy, Design007
Andy Shaughnessy chats with Lawrence Romine about Altium’s new subscription model for their Altium 365 platform. They discuss what this means for existing and future Altium customers, and some of the drivers leading to this development, including evolving use patterns among customers during the pandemic.

Seven Tips for Your Next Stackup Design

02/01/2021 | Eric Bogatin, University of Colorado, Boulder
Rarely do we have the luxury of designing a board just for connectivity. When interconnects are not transparent, we must engineer them to reduce the noise they can generate. This is where design for signal integrity, power integrity and EMC—collectively high-speed digital engineering—are so important. Eric Bogatin offers seven tips for stackup design.

TTM’s Approach to Stackup Design: Train the Customer

01/12/2021 | I-Connect007 Editorial Team
In this interview with the I-Connect007 Editorial Team, TTM’s Julie Ellis and Richard Dang drill down into stackup design, detailing some of the common stackup challenges that their customers face when designing for both prototype and volume levels, and offering advice to designers or engineers who are struggling with stackup issues. They also discuss why having too many different prepregs in a stackup can be asking for trouble, and how proper stackup design can optimize both the fabrication and assembly processes.



Copyright © 2021 I-Connect007. All rights reserved.