The Degrees of Nickel Hyper-corrosion and Mitigation Strategies


Reading time ( words)

Introduction

In previous columns, I presented information on electroless nickel-immersion gold and possible concerns with black pad and brittle fracture. I am a firm believer (as well as a stickler) for tight process control. In addition, this also means that understanding the root cause or causes of defects must be pursued with vigor!

As a case in point, in this month’s column, I will present additional information about nickel hyper-corrosion by further defining the five degrees of hyper-corrosion. This implies that certain levels of the attack on the nickel are more detrimental than others. It should be noted that for purposes of this writing, I define hyper-corrosion as a spike or fissure in the nickel deposit evident after immersion gold plating. Finally the root causes of such attack on the base nickel will be presented along with strategies to mitigate these effects.

The Five Degrees of Hyper-corrosion

As the title of this column implies, we have identified five degrees of hyper-corrosion. While somewhat arbitrary, the extent of the corrosion spikes or fissures are responsible for the rating given. We found it necessary to provide this input to the industry as we found that, all too often, the OEM sees a tiny fissure in the nickel deposit and makes the false assumption that the PCB will fail in some way. That is categorically false, and I will explain why. First, however, let’s review the definition of each of the degrees of hyper-corrosion:

  1. Level 1: Only a few spike-type defects and not on every pad observed.
  2. Level 2: A few spike-type defects observed on most pads.
  3. Level 3: More than a few spike-type defects and some spreader/spike defects on most pads observed. At this activity level, more than 99% of the solder surface has not degraded or shown signs of increased phosphorus and as such should not inhibit intermetallic formation.
  4. Level 4: More spreader/spike defects and some area black band defects on most pads observed. This activity level may degrade solder joint integrity.
  5. Level 5: Mostly large areas of continuous black band on many pads observed. This level of defect activity will affect solder joint integrity.

Read the full column here.


Editor's Note: This column originally appeared in the June 2014 issue of The PCB Magazine.

Share




Suggested Items

Michael Carano: A Focus on Process Control, Part 2

09/28/2022 | I-Connect007 Editorial Team
In this second half of our conversation, Michael Carano discusses some of the metrics that fabricators need to consider before investing in new processes, especially process control technologies, and some of the challenges board shops face updating brownfield sites.

A Focus on Process Control, Part 1

09/27/2022 | I-Connect007 Editorial Team
Michael Carano is a noted subject matter expert with respect to process control, electroplating and metallization technology, surface finishing, and reliability. So, it was only natural that we sat down to talk about mechanizing an existing facility given today’s fickle environment. Will any of the CHIPS funding trickle down to bare board fabrication? What process can be adjusted on the factory floor? The focus needs to be more than just on manufacturing and getting work out the door, he says, but also process control.

EIPC Summer Conference 2022: Day 2 Review

06/29/2022 | Pete Starkey, I-Connect007
Örebro, Sweden on June 15 brought a bright and early start to Day 2 of the EIPC Summer Conference for those who had enjoyed the previous evening’s networking dinner, but had resisted the temptation to over-indulge or to carry on their long-awaited catch-up conversations with old friends into the small hours. All but a few were in their seats for 9 a.m., awake and attentive for Session 4 of the conference, on the theme of new process technologies, moderated by Martyn Gaudion, CEO of Polar Instruments.



Copyright © 2022 I-Connect007. All rights reserved.