- News
- Books
Featured Books
- pcb007 Magazine
Latest Issues
Current IssueAdditive Manufacturing
In this month’s issue, we explore additive manufacturing technology for the PCB fabricator: where it stands today, the true benefits, and where it seems to be headed.
The Growing Industry
In this issue of PCB007 Magazine, we talk with leading economic experts, advocacy specialists in Washington, D.C., and PCB company leadership to get a well-rounded picture of what’s happening in the industry today. Don’t miss it.
The Sustainability Issue
Sustainability is one of the most widely used terms in business today, especially for electronics and manufacturing but what does it mean to you? We explore the environmental, business, and economic impacts.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - pcb007 Magazine
Estimated reading time: 1 minute
Contact Columnist Form
Getting to the Root Cause - Solderability Defect Analysis
In this case study, the PCB fabricator investigates the root cause of solderability defects on ENIG-processed circuits. It was determined that the fabricator, due to process errors, caused hyper-corrosion within the nickel deposit, which led to the defects.
Introduction
A PCB fabricator received a number of returned PCBs from one of its assembly customers. The issue, according to the assembly team, was dewetting, and in some cases, non-wetting of surface mount pads. In addition, some of those components failed to make a reliable bond to the pad, leading to significant failures. And as so often is the case, someone invokes the ghost of black pad as the culprit. Certainly while such an anomaly is a possibility with respect to the root cause failure mechanism, this case requires significant study in order to properly reach a solution to the problem.
Problem Identification
First, one must identify the problem or defect (Figure 1 and Figure 2).
Figure 1: Note area where solder did not completely wet-out.
I consider this a very minor issue considering the board design, reflow temperatures, and paste print could have a great deal to do with what is seen here.
Figure 2: Some additional dewetting.
Read the full column here.Editor's Note: This column originally appeared in the December 2014 issue of The PCB Magazine.
More Columns from Trouble in Your Tank
Trouble in Your Tank: Supporting IC Substrates and Advanced Packaging, Part 5Trouble in Your Tank: Electrodeposition of Copper, Part 6
Trouble in Your Tank: Electrolytic Copper Plating, Part 5
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 4
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 3
Trouble in Your Tank: Electrodeposition of Copper, Part 4—Addition Agents
Trouble in Your Tank: Lead-free and the Fabrication Challenge, Part 1
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 2